- 密度 [g/cm3]: 1.71
- 缺口沖擊強度: 14.4
- 斷裂伸長率 [%]: 330
- 彎曲強度 [MPa]: 186.0
- 彎曲模量 [MPa]: 14.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in3 | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 186 MPa | 27000 psi | ASTM D638 |
| Flexural Yield Strength | 330 MPa | 47900 psi | ASTM D790 |
| Flexural Modulus | 14.5 GPa | 2100 ksi | ASTM D790 |
| Compressive Yield Strength | 196 MPa | 28400 psi | ASTM D695 |
| Izod Impact, Notched | 14.4 J/cm | 27.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 190 °C | 374 °F | Long Term |
| Shrinkage | 0.00050 % | 0.00050 % | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 132 - 160 °C | 270 - 320 °F | Mold temperature |