- 密度 [g/cm3]: 1.32
- 吸水率 [%]: 0.07
- 缺口沖擊強度: 10.0
- 拉伸強度 [MPa]: 95.0
- 彎曲模量 [MPa]: 7.60
- 熱變形溫度 [℃]: 255.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in3 | ISO 1183 B |
| Filler Content | 22 % | 22 % | Glass |
| Water Absorption | 0.070 % | 0.070 % | 24 hours |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm @Thickness 2.00 mm | 0.0020 - 0.0040 in/in @Thickness 0.0787 in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0090 cm/cm @Thickness 2.00 mm | 0.0050 - 0.0090 in/in @Thickness 0.0787 in | ISO 294 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 95.0 MPa | 13800 psi | ISO 527 |
| Elongation at Break | 2.3 % | 2.3 % | ISO 527 |
| Tensile Modulus | 7.00 GPa | 1020 ksi | ISO 527 |
| Flexural Strength | 150 MPa | 21800 psi | ISO 178 |
| Flexural Modulus | 7.60 GPa | 1100 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 180 |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m2 | 21.4 ft-lb/in2 | ISO 180 |
| Charpy Impact Unnotched | 3.50 J/cm2 @Temperature 23.0 °C | 16.7 ft-lb/in2 @Temperature 73.4 °F | ISO 179 |
| Charpy Impact, Notched | 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.80e+20 ohm-cm | 1.80e+20 ohm-cm | IEC 93 |
| Dielectric Constant | 3.0 | 3.0 | IEC 250 |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | ASTM D149 |
| Dissipation Factor | 0.0010 | 0.0010 | IEC 250 |
| Comparative Tracking Index | 450 V | 450 V | Solution A; IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 24.0 μm/m-°C @Temperature 100 °C | 13.3 μin/in-°F @Temperature 212 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 255 °C | 491 °F | ISO 75B |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75A |
| Vicat Softening Point | 255 °C | 491 °F | A/10N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |
| Oxygen Index | 26 % | 26 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 1.00 mm | 1760 °F @Thickness 0.0394 in | IEC 695-2-1 |
| 960 °C @Thickness 2.00 mm | 1760 °F @Thickness 0.0787 in | IEC 695-2-1 | |
| 960 °C @Thickness 3.00 mm | 1760 °F @Thickness 0.118 in | IEC 695-2-1 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 285 - 310 °C | 545 - 590 °F | pre-drying not required |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| 140 - 155 °C | 284 - 311 °F | for optimal gloss and heat resistance | |