- 密度 [g/cm3]: 1.08
- 吸水率 [%]: 0.009
- 缺口沖擊強(qiáng)度: 0.427
- 拉伸強(qiáng)度 [MPa]: 92.0
- 斷裂伸長率 [%]: 103
- 彎曲強(qiáng)度 [MPa]: 65.5
- 彎曲模量 [MPa]: 4.14
- 熱變形溫度 [℃]: 238.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 - 1.54 g/cc | 0.0390 - 0.0556 lb/in3 | Average value: 1.29 g/cc Grade Count:59 |
| Filler Content | 10.0 - 40.0 % | 10.0 - 40.0 % | Average value: 27.3 % Grade Count:34 |
| Water Absorption | 0.00900 - 0.0900 % | 0.00900 - 0.0900 % | Average value: 0.0166 % Grade Count:33 |
| Moisture Absorption at Equilibrium | 0.0100 - 0.450 % | 0.0100 - 0.450 % | Average value: 0.0964 % Grade Count:10 |
| Linear Mold Shrinkage | 0.00100 - 0.00900 cm/cm | 0.00100 - 0.00900 in/in | Average value: 0.00301 cm/cm Grade Count:46 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.0110 cm/cm | 0.00200 - 0.0110 in/in | Average value: 0.00713 cm/cm Grade Count:18 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 65.5 - 134 MPa | 9500 - 19500 psi | Average value: 108 MPa Grade Count:46 |
| Tensile Strength, Yield | 92.0 - 175 MPa | 13300 - 25400 psi | Average value: 115 MPa Grade Count:28 |
| Elongation at Break | 0.600 - 3.00 % | 0.600 - 3.00 % | Average value: 1.69 % Grade Count:41 |
| Modulus of Elasticity | 4.14 - 24.1 GPa | 600 - 3500 ksi | Average value: 9.88 GPa Grade Count:48 |
| Flexural Yield Strength | 103 - 260 MPa | 15000 - 37700 psi | Average value: 164 MPa Grade Count:41 |
| Flexural Modulus | 4.14 - 24.1 GPa | 600 - 3500 ksi | Average value: 9.92 GPa Grade Count:46 |
| Izod Impact, Notched | 0.427 - 1.49 J/cm | 0.800 - 2.80 ft-lb/in | Average value: 0.876 J/cm Grade Count:48 |
| 1.17 - 1.17 J/cm @Temperature -17.8 - -17.8 °C | 2.19 - 2.19 ft-lb/in @Temperature -0.0400 - -0.0400 °F | Average value: 1.17 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 1.44 - 13.3 J/cm | 2.70 - 25.0 ft-lb/in | Average value: 4.11 J/cm Grade Count:27 |
| Izod Impact, Notched (ISO) | 3.70 - 14.0 kJ/m2 | 1.76 - 6.66 ft-lb/in2 | Average value: 9.25 kJ/m2 Grade Count:13 |
| Izod Impact, Unnotched (ISO) | 17.0 - 55.0 kJ/m2 | 8.09 - 26.2 ft-lb/in2 | Average value: 42.5 kJ/m2 Grade Count:11 |
| Charpy Impact Unnotched | 3.40 - 6.10 J/cm2 | 16.2 - 29.0 ft-lb/in2 | Average value: 4.02 J/cm2 Grade Count:9 |
| Charpy Impact, Notched | 0.700 - 1.20 J/cm2 | 3.33 - 5.71 ft-lb/in2 | Average value: 0.930 J/cm2 Grade Count:9 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.30e+12 - 1.80e+20 ohm-cm | 1.30e+12 - 1.80e+20 ohm-cm | Average value: 1.81e+19 ohm-cm Grade Count:10 |
| Dielectric Constant | 3.00 - 3.20 | 3.00 - 3.20 | Average value: 3.12 Grade Count:11 |
| Dielectric Strength | 17.0 - 35.0 kV/mm | 432 - 889 kV/in | Average value: 24.5 kV/mm Grade Count:27 |
| Dissipation Factor | 0.00100 - 0.0690 | 0.00100 - 0.0690 | Average value: 0.00642 Grade Count:19 |
| Comparative Tracking Index | 250 - 600 V | 250 - 600 V | Average value: 464 V Grade Count:16 |
| Hot Wire Ignition, HWI | 15.0 - 107 sec | 15.0 - 107 sec | Average value: 58.2 sec Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 16.2 - 42.3 μm/m-°C | 9.00 - 23.5 μin/in-°F | Average value: 26.5 μm/m-°C Grade Count:15 |
| 18.0 - 39.0 μm/m-°C @Temperature 100 - 100 °C | 10.0 - 21.7 μin/in-°F @Temperature 212 - 212 °F | Average value: 26.1 μm/m-°C Grade Count:9 | |
| 17.0 - 17.0 μm/m-°C @Temperature 100 - 100 °C | 9.44 - 9.44 μin/in-°F @Temperature 212 - 212 °F | Average value: 26.1 μm/m-°C Grade Count:1 | |
| 17.0 - 17.0 μm/m-°C @Thickness 3.20 - 3.20 mm | 9.44 - 9.44 μin/in-°F @Thickness 0.126 - 0.126 in | Average value: 26.1 μm/m-°C Grade Count:1 | |
| CTE, linear, Transverse to Flow | 48.0 - 69.0 μm/m-°C | 26.7 - 38.3 μin/in-°F | Average value: 59.7 μm/m-°C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 238 - 263 °C | 460 - 505 °F | Average value: 259 °C Grade Count:28 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 - 263 °C | 219 - 505 °F | Average value: 223 °C Grade Count:47 |
| Vicat Softening Point | 255 - 263 °C | 491 - 505 °F | Average value: 262 °C Grade Count:21 |
| Flammability, UL94 | HB - 5VA | HB - 5VA | Grade Count:28 |
| Glow Wire Test | 650 - 960 °C | 1200 - 1760 °F | Average value: 822 °C Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 271 - 327 °C | 520 - 620 °F | Average value: 299 °C Grade Count:5 |
| Melt Temperature | 270 - 330 °C | 518 - 626 °F | Average value: 306 °C Grade Count:38 |
| Mold Temperature | 40.0 - 155 °C | 104 - 311 °F | Average value: 108 °C Grade Count:43 |
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | Average value: 85.0 °C Grade Count:31 |
| Dry Time | 2.00 - 5.00 hour | 2.00 - 5.00 hour | Average value: 2.22 hour Grade Count:27 |
| Moisture Content | 0.0200 % | 0.0200 % | Average value: 0.0200 % Grade Count:19 |
| Dew Point | -28.9 °C | -20.0 °F | Average value: -28.9 °C Grade Count:19 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:24 |