| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.60 g/cc | 1.60 g/cc | ASTM D792 | ||
| Filler Content | 30 % | 30 % | Glass Fiber Reinforcement | ||
| Water Absorption | <= 0.10 % @Time 86400 sec | <= 0.10 % @Time 24.0 hour | ASTM D570 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength | 135 MPa | 19600 psi | ASTM D638 | ||
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 | ||
| Tensile Modulus | 15.9 GPa | 2310 ksi | ASTM D638 | ||
| Flexural Strength | 172 MPa | 24900 psi | ASTM D790 | ||
| Flexural Modulus | 13.4 GPa | 1940 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 | ||
| 4.30 J/cm | 8.06 ft-lb/in | ASTM D4812 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 | ||
| Dielectric Constant | 3.9 @Frequency 1.00e+6 Hz | 3.9 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 4.2 @Frequency 60.0 Hz | 4.2 @Frequency 60.0 Hz | ASTM D150 | |||
| Dielectric Strength | 1.54 kV/mm @Thickness 1.57 mm | 39.0 kV/in @Thickness 0.0618 in | ASTM D149 | ||
| High Voltage Arc Resistance to Ignition (HVAR) | >= 300 sec | >= 300 sec | UL 746 | ||
| Comparative Tracking Index | 185 V | 185 V | ASTM D3638 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 3.60 - 7.20 μm/m-°C | 2.00 - 4.00 μin/in-°F | ASTM D696 | ||
| CTE, linear, Transverse to Flow | 40.0 - 79.0 μm/m-°C | 22.2 - 43.9 μin/in-°F | ASTM D696 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 271 °C | 520 °F | Unannealed; ASTM D648 | ||
| UL RTI, Electrical | 220 °C @Thickness 0.750 mm | 428 °F @Thickness 0.0295 in | UL 746 | ||
| UL RTI, Mechanical with Impact | 200 °C @Thickness 0.750 mm | 392 °F @Thickness 0.0295 in | UL 746 | ||
| UL RTI, Mechanical without Impact | 220 °C @Thickness 0.750 mm | 428 °F @Thickness 0.0295 in | UL 746 | ||
| Flammability, UL94 | V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | BK; UL 94 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 321 - 360 °C | 610 - 680 °F | |||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Drying Temperature | 149 °C | 300 °F | |||
| Dry Time | 6.00 - 8.00 hour | 6.00 - 8.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Black | ||||
| Natural Color | |||||
| Automotive Specifications | ASTM D5138 LCP0110 G30 B00000 | ||||
| DELPHI M-5282 M5282 Color: BK Black | |||||
| Availability | Asia Pacific | ||||
| Europe | |||||
| North America | |||||
| Clamp Tonnage | 2.8 to 5.5 kN/cm2 | ||||
| Features | Flame Retardant | ||||
| Good Chemical Resistance | |||||
| Good Moldability | |||||
| Good Weather Resistance | |||||
| High Stiffness | |||||
| High Strength | |||||
| Low Warpage | |||||
| Radiation (Gamma) Resistant | |||||
| Forms | Pellets | ||||
| Generic | LCP | ||||
| Processing Method | Injection Molding | ||||
| RoHS Compliance | RoHS Compliant | ||||
| Screw Compression Ratio | 2.5:1.0 to 3.0:1.0 | ||||
| Screw L/D Ratio | 20.0:1.0 to 24.0:1.0 | ||||
| Uses | Automotive Applications | ||||
| Automotive Electronics | |||||
| Bobbins | |||||
| Electrical Parts | |||||
| Electrical/Electronic Applications | |||||
| Industrial Applications | |||||
| Industrial Parts | |||||