- 缺口沖擊強(qiáng)度: 0.534
- 彎曲強(qiáng)度 [MPa]: 86.2
- 彎曲模量 [MPa]: 9.31
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 g/cc | 1.75 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 86.2 MPa | 12500 psi | ASTM D638 |
| Elongation at Break | 3.5 % | 3.5 % | ASTM D638 |
| Tensile Modulus | 12.1 GPa | 1750 ksi | ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | ASTM D570 |
| Flexural Modulus | 9.31 GPa | 1350 ksi | ASTM D570 |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| Izod Impact Unnotched | 14.9 J | 11.0 ft-lb | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 445 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 321 - 360 °C | 610 - 680 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 6 - 8 hour | 6 - 8 hour | |
| Dew Point | -28.9 °C | -20.0 °F | |