- 密度 [g/cm3]: 1.89
- 吸水率 [%]: 0.02
- 缺口沖擊強(qiáng)度: 5.0
- 彎曲強(qiáng)度 [MPa]: 115.0
- 彎曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in3 | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO 527 |
| Elongation at Break | 2.4 % | 2.4 % | IEC 527 |
| Tensile Modulus | 19.0 GPa | 2760 ksi | ISO 527 |
| Flexural Strength | 170 MPa | 24700 psi | ISO 178 |
| Flexural Modulus | 17.0 GPa | 2470 ksi | ISO 178 |
| Compressive Strength | 95.0 MPa | 13800 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 16.5 GPa | 2390 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO 180/1A |
| Charpy Impact, Notched | 0.400 J/cm2 | 1.90 ft-lb/in2 | ISO 179 |
| Tensile Impact Strength | 50.0 kJ/m2 | 23.8 ft-lb/in2 | Notched; ASTM D1822 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 3.7 @Frequency 1e+7 Hz | 3.7 @Frequency 1e+7 Hz | |
| 4.0 @Frequency 1000 Hz | 4.0 @Frequency 1000 Hz | IEC 250 | |
| Dissipation Factor | 0.0070 @Frequency 1e+7 Hz | 0.0070 @Frequency 1e+7 Hz | |
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | IEC 250 | |
| Arc Resistance | 183 sec | 183 sec | |
| Comparative Tracking Index | 225 V | 225 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 1.00 μm/m-°C @Temperature -50.0 - 200 °C | 0.556 μin/in-°F @Temperature -58.0 - 392 °F | Flow Direction |
| 1.00 μm/m-°C @Temperature -58.0 - 390 °C | 0.556 μin/in-°F @Temperature -72.4 - 734 °F | Flow Direction | |
| CTE, linear, Transverse to Flow | 60.0 μm/m-°C @Temperature -50.0 - 200 °C | 33.3 μin/in-°F @Temperature -58.0 - 392 °F | |
| 60.0 μm/m-°C @Temperature -50.0 - 200 °C | 33.3 μin/in-°F @Temperature -58.0 - 392 °F | ||
| Melting Point | 325 °C | 617 °F | ISO 3146 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75/A |
| UL RTI, Electrical | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | Generic Rating for Vectra LCP |