- 密度 [g/cm3]: 1.89
- 吸水率 [%]: 0.02
- 缺口沖擊強(qiáng)度: 6.0
- 彎曲強(qiáng)度 [MPa]: 145.0
- 彎曲模量 [MPa]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in3 | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm | 0.0020 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 79 | 79 | ISO 2039-2 |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | ISO 527 |
| Elongation at Break | 1.4 % | 1.4 % | IEC 527 |
| Tensile Modulus | 22.0 GPa | 3190 ksi | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 20.0 GPa | 2900 ksi | ISO 178 |
| Compressive Strength | 131 MPa | 19000 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 21.5 GPa | 3120 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 | 2.86 ft-lb/in2 | ISO 180/1A |
| Charpy Impact, Notched | 0.800 J/cm2 | 3.81 ft-lb/in2 | ISO 179 |
| Coefficient of Friction, Dynamic | 0.17 | 0.17 | vs. steel; ASTM D1984 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 5.9 @Frequency 1e+7 Hz | 5.9 @Frequency 1e+7 Hz | |
| 6.7 @Frequency 1000 Hz | 6.7 @Frequency 1000 Hz | IEC 250 | |
| Dissipation Factor | 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | IEC 250 |
| 0.020 @Frequency 1e+7 Hz | 0.020 @Frequency 1e+7 Hz | ||
| Arc Resistance | 180 sec | 180 sec | |
| Comparative Tracking Index | 250 V | 250 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 11.0 μm/m-°C @Temperature -50.0 - 200 °C | 6.11 μin/in-°F @Temperature -58.0 - 392 °F | Flow Direction |
| 11.0 μm/m-°C @Temperature -58.0 - 390 °C | 6.11 μin/in-°F @Temperature -72.4 - 734 °F | Flow Direction | |
| CTE, linear, Transverse to Flow | 51.0 μm/m-°C @Temperature -50.0 - 200 °C | 28.3 μin/in-°F @Temperature -58.0 - 392 °F | |
| 51.0 μm/m-°C @Temperature -50.0 - 200 °C | 28.3 μin/in-°F @Temperature -58.0 - 392 °F | ||
| Melting Point | 280 °C | 536 °F | ISO 3146 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75/A |
| Vicat Softening Point | 238 °C | 460 °F | ASTM D1525 |
| UL RTI, Electrical | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Flammability, UL94 | V-0 | V-0 | |