- 密度 [g/cm3]: 1.73
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 7.0
- 彎曲模量 [MPa]: 13.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.73 g/cc | 0.0625 lb/in3 | ISO 1183 |
| Water Absorption at Saturation | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 112 MPa | 16200 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 13.1 GPa | 1900 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 163 MPa | 23600 psi | ISO 178 |
| Flexural Modulus | 13.2 GPa | 1910 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 20.0 kJ/m2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1U |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 |
| 4.4 @Frequency 100 Hz | 4.4 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 34.0 kV/mm | 864 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.013 @Frequency 100 Hz | 0.013 @Frequency 100 Hz | IEC 60250 |
| 0.023 @Frequency 1.00e+6 Hz | 0.023 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 6.00 μm/m-°C | 3.33 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 50.0 μm/m-°C | 27.8 μin/in-°F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 269 °C | 516 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 150 °C | 104 - 302 °F | cavity |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3 hour | 3 hour | |
| Moisture Content | 0.010 % | 0.010 % | Necessary low maximum |