- 密度 [g/cm3]: 1.76
- 吸水率 [%]: 0.02
- 缺口沖擊強(qiáng)度: 20.0
- 彎曲強(qiáng)度 [MPa]: 155.0
- 彎曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in3 | ISO 1183 |
| Water Absorption | 0.020 % | 0.020 % | Immersion to equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.020 % | 0.020 % | ISO 62 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0040 cm/cm | 0.0040 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 63 | 63 | ISO 2039-2 |
| Tensile Strength, Ultimate | 155 MPa | 22500 psi | ISO 527 |
| Elongation at Break | 3.9 % | 3.9 % | IEC 527 |
| Tensile Modulus | 19.0 GPa | 2760 ksi | ISO 527 |
| Flexural Strength | 195 MPa | 28300 psi | ISO 178 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | ISO 178 |
| Compressive Strength | 78.0 MPa | 11300 psi | 1% Deflection, ISO 604 |
| Compressive Modulus | 12.0 GPa | 1740 ksi | ISO 604 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m2 | 9.52 ft-lb/in2 | ISO 180/1A |
| Charpy Impact, Notched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO 179 |
| Tensile Impact Strength | 40.0 kJ/m2 | 19.0 ft-lb/in2 | Notched; ASTM D1822 |
| Coefficient of Friction, Dynamic | 0.12 | 0.12 | vs. steel; ASTM D1984 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | IEC 93 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | IEC 93 |
| Dielectric Constant | 3.7 @Frequency 1e+7 Hz | 3.7 @Frequency 1e+7 Hz | |
| 4.2 @Frequency 1000 Hz | 4.2 @Frequency 1000 Hz | IEC 250 | |
| Dissipation Factor | 0.0080 @Frequency 1e+7 Hz | 0.0080 @Frequency 1e+7 Hz | |
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | IEC 250 | |
| Arc Resistance | 180 sec | 180 sec | |
| Comparative Tracking Index | 200 V | 200 V | IEC 112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.000 μm/m-°C @Temperature -50.0 - 200 °C | 0.000 μin/in-°F @Temperature -58.0 - 392 °F | Flow Direction |
| 0.000 μm/m-°C @Temperature -58.0 - 390 °C | 0.000 μin/in-°F @Temperature -72.4 - 734 °F | Flow Direction | |
| CTE, linear, Transverse to Flow | 50.0 μm/m-°C @Temperature -50.0 - 200 °C | 27.8 μin/in-°F @Temperature -58.0 - 392 °F | |
| 50.0 μm/m-°C @Temperature -50.0 - 200 °C | 27.8 μin/in-°F @Temperature -58.0 - 392 °F | ||
| Melting Point | 280 °C | 536 °F | ISO 3146 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75/A |
| UL RTI, Electrical | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| UL RTI, Mechanical with Impact | 130 °C | 266 °F | Generic Rating for Vectra LCP |
| Flammability, UL94 | V-0 | V-0 | |