- 密度 [g/cm3]: 1.63
- 彎曲模量 [MPa]: 9.60
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 4.00 % | 4.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.5 GPa | 1520 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 |
| Flexural Modulus | 9.60 GPa | 1390 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 239 °C | 462 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Zone 1 | 335 - 345 °C | 635 - 653 °F | |
| Zone 2 | 350 - 360 °C | 662 - 680 °F | |
| Zone 3 | 350 - 360 °C | 662 - 680 °F | |
| Zone 4 | 350 - 360 °C | 662 - 680 °F | |
| Die Temperature | 350 - 360 °C | 662 - 680 °F | |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Back Pressure | 3.00 MPa | 435 psi | |