- 密度 [g/cm3]: 1.71
- 缺口沖擊強度: 12.0
- 彎曲模量 [MPa]: 16.5
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.71 g/cc | 0.0618 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.000500 cm/cm | 0.000500 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 1.10 % | 1.10 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 17.0 GPa | 2470 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 16.5 GPa | 2390 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m2 | 5.71 ft-lb/in2 | ISO 180/1A |
| Charpy Impact Unnotched | 2.30 J/cm2 | 10.9 ft-lb/in2 | ISO 179/1eU |
| 2.00 J/cm2 @Temperature -30.0 °C | 9.52 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 1.50 J/cm2 | 7.14 ft-lb/in2 | ISO 179/1eA |
| 1.50 J/cm2 @Temperature -30.0 °C | 7.14 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Strength | 45.0 kV/mm | 1140 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 4.00 μm/m-°C | 2.22 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 64.0 μm/m-°C | 35.6 μin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL94 |
| V-0 @Thickness 0.400 mm | V-0 @Thickness 0.0157 in | UL94 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 150 °C | 104 - 302 °F | Cavity temperature |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| 350 - 360 °C | 662 - 680 °F | ||
| 355 °C | 671 °F | Optimum | |
| Mold Temperature | 90.0 °C | 194 °F | Optimum |
| 30.0 - 160 °C | 86.0 - 320 °F | ||
| Drying Temperature | >= 150 °C | >= 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |