- 密度 [g/cm3]: 1.89
- 缺口沖擊強度: 29.0
- 彎曲模量 [MPa]: 12.165
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.89 g/cc | 0.0683 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.00600 cm/cm | 0.00600 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 125 MPa | 18100 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 2.50 % | 2.50 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 14.26 GPa | 2068 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 |
| Flexural Modulus | 12.165 GPa | 1764.4 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 29.0 kJ/m2 | 13.8 ft-lb/in2 | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 | 16.7 ft-lb/in2 | ISO 180/1U |
| Charpy Impact Unnotched | 3.60 J/cm2 | 17.1 ft-lb/in2 | ISO 179/1eU |
| Charpy Impact, Notched | 3.00 J/cm2 | 14.3 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Dielectric Constant | 4.52 @Frequency 1.00e+6 Hz | 4.52 @Frequency 1.00e+6 Hz | IEC 60250 |
| 6.07 @Frequency 2.05e+9 Hz | 6.07 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 | |
| Dissipation Factor | 0.00400 @Frequency 2.05e+9 Hz | 0.00400 @Frequency 2.05e+9 Hz | IPC TM-650 2.5.5.13 |
| 0.0190 @Frequency 1.00e+6 Hz | 0.0190 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 276 °C | 529 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |
| Feed Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |
| Zone 1 | 320 - 330 °C | 608 - 626 °F | |
| Zone 2 | 335 - 345 °C | 635 - 653 °F | |
| Zone 3 | 335 - 345 °C | 635 - 653 °F | |
| Zone 4 | 335 - 345 °C | 635 - 653 °F | |
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |
| Melt Temperature | 330 - 350 °C | 626 - 662 °F | |
| Drying Temperature | >= 150 °C | >= 302 °F | |
| Dry Time | 5.00 hour | 5.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |
| Back Pressure | 3.00 MPa | 435 psi | |