- 密度 [g/cm3]: 1.76
- 缺口沖擊強度: 8.0
- 彎曲模量 [MPa]: 12.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.00200 cm/cm | 0.00200 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.40 % | 1.40 % | 5mm/min; ISO 527-2/1A | ||
| 2.00 % | 2.00 % | Flexural strain; ISO 178 | |||
| Tensile Modulus | 12.0 GPa | 1740 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 | ||
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 8.00 kJ/m2 | 3.81 ft-lb/in2 | ISO 180/1A | ||
| Charpy Impact Unnotched | 1.00 J/cm2 | 4.76 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.600 J/cm2 | 2.86 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 | ||
| Dielectric Constant | 4.00 @Frequency 1.00e+6 Hz | 4.00 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.00700 @Frequency 1.00e+6 Hz | 0.00700 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 150 V | 150 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 8.00 μm/m-°C | 4.44 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 17.0 μm/m-°C | 9.44 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 315 °C | 599 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 271 °C | 520 °F | ISO 75-1, -2 | ||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 330 - 350 °C | 626 - 662 °F | |||
| Zone 2 | 340 - 360 °C | 644 - 680 °F | |||
| Zone 3 | 345 - 365 °C | 653 - 689 °F | |||
| Zone 4 | 355 - 370 °C | 671 - 698 °F | |||
| Die Temperature | 355 - 370 °C | 671 - 698 °F | |||
| Melt Temperature | 360 - 375 °C | 680 - 707 °F | |||
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Hot-Working Temperature | 355 - 370 °C | 671 - 698 °F | |||
| Descriptive Properties | |||||
| Injection speed | medium | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||