- 密度 [g/cm3]: 1.65
- 彎曲模量 [MPa]: 12.0
- 熱變形溫度 [℃]: 284.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.000500 cm/cm | 0.000500 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00430 cm/cm | 0.00430 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | 50mm/min; ISO 527-2/1A | ||
| Elongation at Break | 2.00 % | 2.00 % | 50mm/min; ISO 527-2/1A | ||
| 2.50 % | 2.50 % | Flexural strain; ISO 178 | |||
| Tensile Modulus | 12.0 GPa | 1740 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 140 MPa | 20300 psi | ISO 178 | ||
| Flexural Modulus | 12.0 GPa | 1740 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 3.00 J/cm2 | 14.3 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.800 J/cm2 | 3.81 ft-lb/in2 | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 8.00 μm/m-°C | 4.44 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 43.0 μm/m-°C | 23.9 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 331 °C | 628 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 284 °C | 543 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 130 °C | 176 - 266 °F | Cavity temperature | ||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 3 | 330 - 350 °C | 626 - 662 °F | |||
| Zone 4 | 330 - 350 °C | 626 - 662 °F | |||
| Die Temperature | 330 - 340 °C | 626 - 644 °F | |||
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Screw Speed | 100 rpm @Diameter 40.0 mm | 100 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Descriptive Properties | |||||
| Injection speed | medium-fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Short metering strokes | accumulator is recommended | to get short injection times | |||