- 密度 [g/cm3]: 1.64
- 彎曲模量 [MPa]: 9.50
- 熱變形溫度 [℃]: 275.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.64 g/cc | 0.0592 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage, Transverse | 0.00650 cm/cm | 0.00650 in/in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 130 MPa | 18900 psi | 5mm/min; ISO 527-2/1A |
| Elongation at Break | 5.00 % | 5.00 % | 5mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Modulus | 9.50 GPa | 1380 ksi | ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm2 | 28.6 ft-lb/in2 | ISO 179/1eU |
| 4.00 J/cm2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.900 J/cm2 | 4.28 ft-lb/in2 | ISO 179/1eA |
| 0.800 J/cm2 @Temperature -30.0 °C | 3.81 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.40 @Frequency 1.00e+6 Hz | 3.40 @Frequency 1.00e+6 Hz | IEC 60250 |
| 3.80 @Frequency 100 Hz | 3.80 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 |
| Dissipation Factor | 0.0140 @Frequency 100 Hz | 0.0140 @Frequency 100 Hz | IEC 60250 |
| 0.0310 @Frequency 1.00e+6 Hz | 0.0310 @Frequency 1.00e+6 Hz | IEC 60250 | |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 8.00 μm/m-°C | 4.44 μin/in-°F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 40.0 μm/m-°C | 22.2 μin/in-°F | ISO 11359-2 |
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Transformation Temperature, Tg | 120 °C | 248 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 275 °C | 527 °F | ISO 75-1, -2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1, -2 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL94 |
| V-0 @Thickness 0.850 mm | V-0 @Thickness 0.0335 in | UL94 | |
| Oxygen Index | 47.0 % | 47.0 % | ISO 4589 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 40.0 - 150 °C | 104 - 302 °F | Cavity temperature |
| Melt Temperature | 350 - 360 °C | 662 - 680 °F | |
| 350 - 360 °C | 662 - 680 °F | ||
| 355 °C | 671 °F | Optimum | |
| Mold Temperature | 90.0 °C | 194 °F | Optimum |
| 30.0 - 160 °C | 86.0 - 320 °F | ||
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 3.00 hour | 3.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |