- 密度 [g/cm3]: 1.74
- 拉伸強度 [MPa]: 110.0
- 彎曲模量 [MPa]: 11.7
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 110 MPa | 16000 psi | 50mm/min; ISO 527-2/1A |
| Elongation at Yield | 3.20 % | 3.20 % | 50mm/min; ISO 527-2/1A |
| Tensile Modulus | 10.7 GPa | 1550 ksi | 1mm/min; ISO 527-2/1A |
| Flexural Strength | 130 MPa | 18900 psi | ISO 178 |
| Flexural Modulus | 11.7 GPa | 1700 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 357 °C | 675 °F | 10°C/min; ISO 11357-1,-2,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75-1, -2 |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 150 °C | 302 °F | |
| Dry Time | 6.00 hour | 6.00 hour | |
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual |