- 密度 [g/cm3]: 1.74
- 缺口沖擊強度: 5.2
- 彎曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Transverse | 0.00500 cm/cm | 0.00500 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 105 MPa | 15200 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 3.20 % | 3.20 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 9.80 GPa | 1420 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 125 MPa | 18100 psi | ISO 178 | ||
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.20 kJ/m2 | 2.47 ft-lb/in2 | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 35.0 kJ/m2 | 16.7 ft-lb/in2 | ISO 180/1U | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | ||
| Dielectric Constant | 3.60 @Frequency 1.00e+6 Hz | 3.60 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 46.0 kV/mm | 1170 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0310 @Frequency 1.00e+6 Hz | 0.0310 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 11.0 μm/m-°C | 6.11 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 11.0 μm/m-°C | 6.11 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 195 °C | 383 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 320 - 330 °C | 608 - 626 °F | |||
| Zone 3 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 4 | 330 - 340 °C | 626 - 644 °F | |||
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Melt Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Drying Temperature | 170 °C | 338 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm | 80.0 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Descriptive Properties | |||||
| Injection speed | very fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Short metering strokes | accumulator is recommended | to get short injection times | |||