- 密度 [g/cm3]: 1.77
- 吸水率 [%]: 0.005
- 缺口沖擊強度: 9.0
- 彎曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.77 g/cc | 0.0639 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.00500 % | 0.00500 % | ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00140 cm/cm | 0.00140 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00430 cm/cm | 0.00430 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 54.0 | 54.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 110 MPa | 16000 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.50 % | 1.50 % | 5mm/min; ISO 527-2/1A | ||
| 1.80 % | 1.80 % | Flexural strain; ISO 178 | |||
| Tensile Modulus | 13.0 GPa | 1890 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 | ||
| Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 | ||
| Compressive Modulus | 11.0 GPa | 1600 ksi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m2 | 13.3 ft-lb/in2 | ISO 180/1U | ||
| Charpy Impact Unnotched | 2.90 J/cm2 | 13.8 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 1.80 J/cm2 | 8.57 ft-lb/in2 | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 | ||
| Dielectric Constant | 4.24 @Frequency 1.00e+6 Hz | 4.24 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 55.0 kV/mm | 1400 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0450 @Frequency 1.00e+6 Hz | 0.0450 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 8.00 μm/m-°C | 4.44 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 42.0 μm/m-°C | 23.3 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 335 °C | 635 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 200 °C | 392 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 @Thickness 0.150 mm | V-0 @Thickness 0.00591 in | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | ||
| Zone 1 | 315 - 325 °C | 599 - 617 °F | |||
| Zone 2 | 325 - 335 °C | 617 - 635 °F | |||
| Zone 3 | 335 - 345 °C | 635 - 653 °F | |||
| Zone 4 | 340 - 360 °C | 644 - 680 °F | |||
| Die Temperature | 335 - 345 °C | 635 - 653 °F | |||
| Melt Temperature | 340 - 355 °C | 644 - 671 °F | |||
| Drying Temperature | >= 150 °C | >= 302 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Descriptive Properties | |||||
| Injection speed | very fast | ||||