- 密度 [g/cm3]: 1.5
- 缺口沖擊強度: 7.0
- 彎曲模量 [MPa]: 26.0
- 熱變形溫度 [℃]: 250.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in3 | ISO 1183 | ||
| Moisture Absorption | 0.0600 % | 0.0600 % | 23°C/50%RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.00100 cm/cm | 0.00100 in/in | ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.00300 cm/cm | 0.00300 in/in | ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 83.0 | 83.0 | ISO 2039-2 | ||
| Tensile Strength at Break | 149 MPa | 21600 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 1.10 % | 1.10 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 23.5 GPa | 3410 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 228 MPa | 33100 psi | ISO 178 | ||
| Flexural Modulus | 26.0 GPa | 3770 ksi | ISO 178 | ||
| Compressive Strength | 136 MPa | 19700 psi | 1% strain; ISO 604 | ||
| Compressive Modulus | 23.5 GPa | 3410 ksi | ISO 604 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | ISO 180/1A | ||
| Izod Impact, Unnotched (ISO) | 18.0 kJ/m2 | 8.57 ft-lb/in2 | ISO 180/1U | ||
| Charpy Impact Unnotched | 1.30 J/cm2 | 6.19 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179/1eA | ||
| Tensile Creep Modulus, 1 hour | 19600 MPa | 2.84e+6 psi | ISO 899-1 | ||
| Tensile Creep Modulus, 1000 hours | 15800 MPa | 2.29e+6 psi | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100 ohm-cm | 100 ohm-cm | IEC 60093 | ||
| Surface Resistance | 10.0 ohm | 10.0 ohm | IEC 60093 | ||
| Dielectric Constant | 16.09 @Frequency 1.00e+6 Hz | 16.09 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.0257 @Frequency 1.00e+6 Hz | 0.0257 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 2.00 μm/m-°C | 1.11 μin/in-°F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 6.00 μm/m-°C | 3.33 μin/in-°F | ISO 11359-2 | ||
| Melting Point | 280 °C | 536 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 233 °C | 451 °F | ISO 75-1, -2 | ||
| Deflection Temperature at 8.0 MPa | 193 °C | 379 °F | ISO 75-1, -2 | ||
| Vicat Softening Point | 179 °C | 354 °F | B50 (50°C/h 50N); ISO 306 | ||
| Flammability, UL94 | V-0 | V-0 | UL94 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 30.0 °C | 68.0 - 86.0 °F | |||
| 80.0 - 120 °C | 176 - 248 °F | Cavity temperature | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | |||
| Zone 1 | 270 - 280 °C | 518 - 536 °F | |||
| Zone 2 | 275 - 285 °C | 527 - 545 °F | |||
| Zone 3 | 280 - 290 °C | 536 - 554 °F | |||
| Zone 4 | 285 - 295 °C | 545 - 563 °F | |||
| Die Temperature | 290 - 300 °C | 554 - 572 °F | |||
| Melt Temperature | 285 - 295 °C | 545 - 563 °F | |||
| 293 °C | 559 °F | Injection molding; ISO 294 | |||
| Mold Temperature | 60.0 °C | 140 °F | Injection molding; ISO 294 | ||
| Injection Velocity | 150 mm/sec | 5.91 in/sec | ISO 294 | ||
| Drying Temperature | 150 °C | 302 °F | |||
| Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 48.0 MPa | 6960 psi | ISO 294 | ||
| 50.0 - 150 MPa | 7250 - 21800 psi | ||||
| Back Pressure | 3.00 MPa | 435 psi | |||
| Screw Speed | 80.0 rpm @Diameter 40.0 mm | 80.0 rpm @Diameter 1.57 in | |||
| 140 rpm @Diameter 25.0 mm | 140 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 16.0 mm | 200 rpm @Diameter 0.630 in | ||||
| Hot-Working Temperature | 285 - 295 °C | 545 - 563 °F | |||
| Descriptive Properties | |||||
| Injection molding | Yes | ||||
| Injection speed | very fast | ||||
| Longer pre-drying times/storage | 100° C. | <= 60 h | |||
| Short metering strokes | accumulator is recommended | to get short injection times | |||