- 密度 [g/cm3]: 1.74
- 缺口沖擊強度: 5.0
- 彎曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.74 g/cc | 0.0629 lb/in3 | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 105 MPa | 15200 psi | 5mm/min; ISO 527-2/1A | ||
| Elongation at Break | 3.30 % | 3.30 % | 5mm/min; ISO 527-2/1A | ||
| Tensile Modulus | 9.00 GPa | 1310 ksi | 1mm/min; ISO 527-2/1A | ||
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 | ||
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO 180/1A | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 350 °C | 662 °F | 10°C/min; ISO 11357-1,-2,-3 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1, -2 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 20.0 - 60.0 °C | 68.0 - 140 °F | |||
| 80.0 - 140 °C | 176 - 284 °F | Cavity temperature | |||
| Feed Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Zone 1 | 335 - 345 °C | 635 - 653 °F | |||
| Zone 2 | 340 - 350 °C | 644 - 662 °F | |||
| Zone 3 | 345 - 355 °C | 653 - 671 °F | |||
| Zone 4 | 350 - 360 °C | 662 - 680 °F | |||
| Die Temperature | 350 - 360 °C | 662 - 680 °F | |||
| Melt Temperature | 345 - 360 °C | 653 - 680 °F | |||
| Drying Temperature | 150 - 170 °C | 302 - 338 °F | |||
| Dry Time | 6.00 hour | 6.00 hour | |||
| Moisture Content | 0.0100 % | 0.0100 % | Necessary low maximum residual | ||
| Dew Point | <= -40.0 °C | <= -40.0 °F | Pre-drying | ||
| Injection Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | |||
| Screw Speed | 80.0 rpm @Diameter 16.0 mm | 80.0 rpm @Diameter 0.630 in | |||
| 120 rpm @Diameter 25.0 mm | 120 rpm @Diameter 0.984 in | ||||
| 200 rpm @Diameter 40.0 mm | 200 rpm @Diameter 1.57 in | ||||
| Hot-Working Temperature | 365 - 375 °C | 689 - 707 °F | |||
| Descriptive Properties | |||||
| Injection speed | very fast | ||||