- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 0.534
- 斷裂伸長率 [%]: 130
- 彎曲強度 [MPa]: 20.8
- 彎曲模量 [MPa]: 7.20
- 熱變形溫度 [℃]: 270.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 - 1.78 g/cc | 0.0502 - 0.0643 lb/in3 | Average value: 1.70 g/cc Grade Count:34 |
| Filler Content | 40.0 % | 40.0 % | Average value: 40.0 % Grade Count:8 |
| Water Absorption | 0.0200 - 0.100 % | 0.0200 - 0.100 % | Average value: 0.0450 % Grade Count:6 |
| Moisture Absorption at Equilibrium | 0.0100 - 0.0400 % | 0.0100 - 0.0400 % | Average value: 0.0233 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000 - 0.00400 cm/cm | 0.000 - 0.00400 in/in | Average value: 0.00156 cm/cm Grade Count:28 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.0120 cm/cm | 0.00200 - 0.0120 in/in | Average value: 0.00545 cm/cm Grade Count:25 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 44.0 - 96.0 | 44.0 - 96.0 | Average value: 68.0 Grade Count:6 |
| Tensile Strength, Ultimate | 20.8 - 177 MPa | 3020 - 25700 psi | Average value: 116 MPa Grade Count:35 |
| 9.28 - 138 MPa @Temperature -20.0 - 200 °C | 1350 - 20000 psi @Temperature -4.00 - 392 °F | Average value: 49.7 MPa Grade Count:1 | |
| 9.28 - 138 MPa @Strain 0.230 - 4.21 % | 1350 - 20000 psi @Strain 0.230 - 4.21 % | Average value: 49.7 MPa Grade Count:1 | |
| Elongation at Break | 0.500 - 3.50 % | 0.500 - 3.50 % | Average value: 1.66 % Grade Count:35 |
| Modulus of Elasticity | 8.50 - 34.5 GPa | 1230 - 5000 ksi | Average value: 16.1 GPa Grade Count:34 |
| Flexural Yield Strength | 130 - 250 MPa | 18900 - 36300 psi | Average value: 192 MPa Grade Count:35 |
| Flexural Modulus | 7.20 - 27.6 GPa | 1040 - 4000 ksi | Average value: 15.0 GPa Grade Count:35 |
| Compressive Yield Strength | 53.0 - 134 MPa | 7690 - 19400 psi | Average value: 110 MPa Grade Count:5 |
| Compressive Modulus | 7.70 - 18.0 GPa | 1120 - 2610 ksi | Average value: 14.2 GPa Grade Count:5 |
| Izod Impact, Notched | 0.534 - 1.12 J/cm | 1.00 - 2.10 ft-lb/in | Average value: 0.798 J/cm Grade Count:6 |
| Izod Impact, Unnotched | 2.67 - 4.27 J/cm | 5.00 - 8.00 ft-lb/in | Average value: 3.38 J/cm Grade Count:3 |
| Izod Impact, Notched (ISO) | 4.00 - 30.0 kJ/m2 | 1.90 - 14.3 ft-lb/in2 | Average value: 12.0 kJ/m2 Grade Count:17 |
| Izod Impact, Unnotched (ISO) | 14.0 - 45.0 kJ/m2 | 6.66 - 21.4 ft-lb/in2 | Average value: 26.8 kJ/m2 Grade Count:11 |
| 20.0 - 20.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 9.52 - 9.52 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 20.0 kJ/m2 Grade Count:2 | |
| Charpy Impact Unnotched | 2.00 - 5.40 J/cm2 | 9.52 - 25.7 ft-lb/in2 | Average value: 3.05 J/cm2 Grade Count:14 |
| 1.80 - 4.00 J/cm2 @Temperature -30.0 - 30.0 °C | 8.57 - 19.0 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 2.45 J/cm2 Grade Count:4 | |
| Charpy Impact, Notched | 0.500 - 2.70 J/cm2 | 2.38 - 12.8 ft-lb/in2 | Average value: 1.20 J/cm2 Grade Count:24 |
| 0.600 - 1.50 J/cm2 @Temperature -30.0 - 30.0 °C | 2.86 - 7.14 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 1.27 J/cm2 Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 100000 - 1.00e+17 ohm-cm | 100000 - 1.00e+17 ohm-cm | Average value: 9.12e+15 ohm-cm Grade Count:19 |
| Surface Resistance | 1.00e+7 - 1.00e+17 ohm | 1.00e+7 - 1.00e+17 ohm | Average value: 2.49e+16 ohm Grade Count:21 |
| Dielectric Constant | 3.50 - 4.40 | 3.50 - 4.40 | Average value: 3.91 Grade Count:15 |
| Dielectric Strength | 22.6 - 59.0 kV/mm | 575 - 1500 kV/in | Average value: 34.3 kV/mm Grade Count:12 |
| Dissipation Factor | 0.00200 - 0.0280 | 0.00200 - 0.0280 | Average value: 0.0127 Grade Count:15 |
| Arc Resistance | 140 - 180 sec | 140 - 180 sec | Average value: 163 sec Grade Count:4 |
| Comparative Tracking Index | 150 - 249 V | 150 - 249 V | Average value: 181 V Grade Count:15 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 1.00 - 17.0 μm/m-°C | 0.556 - 9.44 μin/in-°F | Average value: 5.13 μm/m-°C Grade Count:25 |
| -2.00 - 3.00 μm/m-°C @Temperature 55.0 - 320 °C | -1.11 - 1.67 μin/in-°F @Temperature 131 - 608 °F | Average value: 1.79 μm/m-°C Grade Count:2 | |
| -2.00 - 5.00 μm/m-°C @Temperature 55.0 - 320 °C | -1.11 - 2.78 μin/in-°F @Temperature 131 - 608 °F | Average value: 1.79 μm/m-°C Grade Count:4 | |
| -2.00 - 5.00 μm/m-°C @Thickness 2.00 - 4.00 mm | -1.11 - 2.78 μin/in-°F @Thickness 0.0787 - 0.157 in | Average value: 1.79 μm/m-°C Grade Count:4 | |
| CTE, linear, Transverse to Flow | 18.0 - 82.0 μm/m-°C | 10.0 - 45.6 μin/in-°F | Average value: 55.7 μm/m-°C Grade Count:25 |
| 71.0 - 88.0 μm/m-°C @Temperature 55.0 - 320 °C | 39.4 - 48.9 μin/in-°F @Temperature 131 - 608 °F | Average value: 84.1 μm/m-°C Grade Count:2 | |
| 71.0 - 94.0 μm/m-°C @Temperature 55.0 - 320 °C | 39.4 - 52.2 μin/in-°F @Temperature 131 - 608 °F | Average value: 84.1 μm/m-°C Grade Count:4 | |
| 71.0 - 94.0 μm/m-°C @Thickness 2.00 - 4.00 mm | 39.4 - 52.2 μin/in-°F @Thickness 0.0787 - 0.157 in | Average value: 84.1 μm/m-°C Grade Count:4 | |
| Melting Point | 280 - 352 °C | 536 - 666 °F | Average value: 329 °C Grade Count:26 |
| Deflection Temperature at 0.46 MPa (66 psi) | 270 - 286 °C | 518 - 547 °F | Average value: 280 °C Grade Count:4 |
| Deflection Temperature at 1.8 MPa (264 psi) | 217 - 356 °C | 423 - 673 °F | Average value: 273 °C Grade Count:35 |
| Deflection Temperature at 8.0 MPa | 130 - 267 °C | 266 - 513 °F | Average value: 206 °C Grade Count:5 |
| Vicat Softening Point | 176 - 224 °C | 349 - 435 °F | Average value: 198 °C Grade Count:5 |
| UL RTI, Electrical | 130 - 240 °C | 266 - 464 °F | Average value: 191 °C Grade Count:5 |
| UL RTI, Mechanical with Impact | 130 - 220 °C | 266 - 428 °F | Average value: 180 °C Grade Count:5 |
| UL RTI, Mechanical without Impact | 130 - 240 °C | 266 - 464 °F | Average value: 199 °C Grade Count:4 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:24 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 391 °C | 68.0 - 735 °F | Average value: 91.7 °C Grade Count:22 |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Average value: 66.4 °C Grade Count:11 |
| Die Temperature | 300 - 380 °C | 572 - 716 °F | Average value: 341 °C Grade Count:16 |
| Melt Temperature | 271 - 385 °C | 520 - 725 °F | Average value: 337 °C Grade Count:31 |
| Mold Temperature | 30.0 - 160 °C | 86.0 - 320 °F | Average value: 90.7 °C Grade Count:16 |
| Drying Temperature | 135 - 170 °C | 275 - 338 °F | Average value: 153 °C Grade Count:28 |
| Dry Time | 3.00 - 24.0 hour | 3.00 - 24.0 hour | Average value: 5.85 hour Grade Count:27 |
| Moisture Content | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:25 |
| Dew Point | -40.0 - -28.9 °C | -40.0 - -20.0 °F | Average value: -39.1 °C Grade Count:11 |
| Injection Pressure | 34.5 - 150 MPa | 5000 - 21800 psi | Average value: 95.4 MPa Grade Count:20 |
| Hold Pressure | 50.0 - 150 MPa | 7250 - 21800 psi | Average value: 100 MPa Grade Count:13 |
| Back Pressure | 3.00 - 3.00 MPa | 435 - 435 psi | Average value: 3.00 MPa Grade Count:10 |
| Screw Speed | 80.0 - 200 rpm | 80.0 - 200 rpm | Average value: 142 rpm Grade Count:14 |
| Hot-Working Temperature | 300 - 370 °C | 572 - 698 °F | Average value: 339 °C Grade Count:9 |