- 密度 [g/cm3]: 1.37
- 吸水率 [%]: 0.02
- 缺口沖擊強度: 0.167
- 斷裂伸長率 [%]: 124
- 彎曲強度 [MPa]: 26.6
- 彎曲模量 [MPa]: 6.60
- 硬度: 105.0
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 - 1.69 g/cc | 0.0495 - 0.0611 lb/in3 | Average value: 1.62 g/cc Grade Count:44 |
| Filler Content | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:12 |
| Water Absorption | 0.0200 - 1.30 % | 0.0200 - 1.30 % | Average value: 0.200 % Grade Count:8 |
| Moisture Absorption at Equilibrium | 0.00200 - 0.0400 % | 0.00200 - 0.0400 % | Average value: 0.0287 % Grade Count:6 |
| Linear Mold Shrinkage | -0.00100 - 0.00400 cm/cm | -0.00100 - 0.00400 in/in | Average value: 0.000889 cm/cm Grade Count:31 |
| Linear Mold Shrinkage, Transverse | 0.00200 - 0.00900 cm/cm | 0.00200 - 0.00900 in/in | Average value: 0.00571 cm/cm Grade Count:25 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 40.0 - 100 | 40.0 - 100 | Average value: 69.3 Grade Count:11 |
| Hardness, Rockwell R | 105 - 118 | 105 - 118 | Average value: 109 Grade Count:6 |
| Tensile Strength, Ultimate | 26.6 - 211 MPa | 3860 - 30600 psi | Average value: 143 MPa Grade Count:43 |
| 14.0 - 250 MPa @Temperature -40.0 - 250 °C | 2030 - 36300 psi @Temperature -40.0 - 482 °F | Average value: 83.4 MPa Grade Count:3 | |
| 14.0 - 250 MPa @Thickness 0.800 - 3.17 mm | 2030 - 36300 psi @Thickness 0.0315 - 0.125 in | Average value: 83.4 MPa Grade Count:3 | |
| 6.97 - 193.7 MPa @Strain 0.0600 - 2.19 % | 1010 - 28090 psi @Strain 0.0600 - 2.19 % | Average value: 83.4 MPa Grade Count:1 | |
| 6.97 - 193.7 MPa @Temperature -40.0 - 200 °C | 1010 - 28090 psi @Temperature -40.0 - 392 °F | Average value: 83.4 MPa Grade Count:1 | |
| Elongation at Break | 1.00 - 4.00 % | 1.00 - 4.00 % | Average value: 2.05 % Grade Count:41 |
| 0.800 - 1.40 % @Temperature -40.0 - 250 °C | 0.800 - 1.40 % @Temperature -40.0 - 482 °F | Average value: 1.14 % Grade Count:1 | |
| 0.800 - 1.40 % @Thickness 1.60 - 1.60 mm | 0.800 - 1.40 % @Thickness 0.0630 - 0.0630 in | Average value: 1.14 % Grade Count:1 | |
| Modulus of Elasticity | 8.27 - 22.0 GPa | 1200 - 3190 ksi | Average value: 14.7 GPa Grade Count:34 |
| 3.40 - 29.0 GPa @Temperature -40.0 - 250 °C | 493 - 4210 ksi @Temperature -40.0 - 482 °F | Average value: 12.3 GPa Grade Count:3 | |
| 3.40 - 29.0 GPa @Thickness 1.60 - 3.17 mm | 493 - 4210 ksi @Thickness 0.0630 - 0.125 in | Average value: 12.3 GPa Grade Count:3 | |
| Flexural Yield Strength | 124 - 300 MPa | 18000 - 43500 psi | Average value: 197 MPa Grade Count:38 |
| 17.0 - 340 MPa @Temperature -40.0 - 250 °C | 2470 - 49300 psi @Temperature -40.0 - 482 °F | Average value: 105 MPa Grade Count:3 | |
| 17.0 - 340 MPa @Thickness 0.800 - 3.17 mm | 2470 - 49300 psi @Thickness 0.0315 - 0.125 in | Average value: 105 MPa Grade Count:3 | |
| Flexural Modulus | 6.60 - 20.0 GPa | 957 - 2900 ksi | Average value: 13.5 GPa Grade Count:43 |
| 2.80 - 25.0 GPa @Temperature -40.0 - 250 °C | 406 - 3630 ksi @Temperature -40.0 - 482 °F | Average value: 9.10 GPa Grade Count:3 | |
| 2.80 - 25.0 GPa @Thickness 0.800 - 3.17 mm | 406 - 3630 ksi @Thickness 0.0315 - 0.125 in | Average value: 9.10 GPa Grade Count:3 | |
| Compressive Yield Strength | 59.0 - 150 MPa | 8560 - 21800 psi | Average value: 108 MPa Grade Count:14 |
| Compressive Modulus | 14.0 - 22.0 GPa | 2030 - 3190 ksi | Average value: 17.1 GPa Grade Count:8 |
| Shear Strength | 51.0 - 68.0 MPa | 7400 - 9860 psi | Average value: 58.2 MPa Grade Count:3 |
| Izod Impact, Notched | 0.167 - 4.30 J/cm | 0.312 - 8.06 ft-lb/in | Average value: 1.71 J/cm Grade Count:18 |
| 1.10 - 4.90 J/cm @Temperature -40.0 - -40.0 °C | 2.06 - 9.18 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 2.67 J/cm Grade Count:3 | |
| 1.10 - 4.90 J/cm @Thickness 0.800 - 3.17 mm | 2.06 - 9.18 ft-lb/in @Thickness 0.0315 - 0.125 in | Average value: 2.67 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 3.47 J/cm - NB | 6.50 ft-lb/in - NB | Average value: 6.24 J/cm Grade Count:9 |
| 5.55 - 475 J/cm @Temperature -40.0 - -40.0 °C | 10.4 - 890 ft-lb/in @Temperature -40.0 - -40.0 °F | Average value: 294 J/cm Grade Count:3 | |
| 5.55 - 475 J/cm @Thickness 0.800 - 3.17 mm | 10.4 - 890 ft-lb/in @Thickness 0.0315 - 0.125 in | Average value: 294 J/cm Grade Count:3 | |
| Izod Impact, Notched (ISO) | 5.00 - 50.5 kJ/m2 | 2.38 - 24.0 ft-lb/in2 | Average value: 19.7 kJ/m2 Grade Count:21 |
| 20.0 - 20.0 kJ/m2 @Temperature -40.0 - -40.0 °C | 9.52 - 9.52 ft-lb/in2 @Temperature -40.0 - -40.0 °F | Average value: 20.0 kJ/m2 Grade Count:1 | |
| Izod Impact, Unnotched (ISO) | 15.0 - 56.6 kJ/m2 | 7.14 - 26.9 ft-lb/in2 | Average value: 32.5 kJ/m2 Grade Count:12 |
| 30.0 - 30.0 kJ/m2 @Temperature -30.0 - -30.0 °C | 14.3 - 14.3 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 30.0 kJ/m2 Grade Count:1 | |
| Charpy Impact Unnotched | 0.600 - 5.00 J/cm2 | 2.86 - 23.8 ft-lb/in2 | Average value: 3.29 J/cm2 Grade Count:17 |
| 2.20 - 3.00 J/cm2 @Temperature -30.0 - 30.0 °C | 10.5 - 14.3 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 2.52 J/cm2 Grade Count:6 | |
| Charpy Impact, Notched | 0.500 - 4.30 J/cm2 | 2.38 - 20.5 ft-lb/in2 | Average value: 2.19 J/cm2 Grade Count:23 |
| 1.50 - 3.00 J/cm2 @Temperature -30.0 - 30.0 °C | 7.14 - 14.3 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 2.29 J/cm2 Grade Count:7 | |
| Tensile Creep Modulus, 1 hour | 12600 - 16000 MPa | 1.83e+6 - 2.32e+6 psi | Average value: 14100 MPa Grade Count:3 |
| Tensile Creep Modulus, 1000 hours | 10900 - 14100 MPa | 1.58e+6 - 2.05e+6 psi | Average value: 12200 MPa Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 - 1.00e+17 ohm-cm | 1.00e+12 - 1.00e+17 ohm-cm | Average value: 5.98e+15 ohm-cm Grade Count:28 |
| Surface Resistance | 1.00e+14 - 1.00e+17 ohm | 1.00e+14 - 1.00e+17 ohm | Average value: 9.04e+15 ohm Grade Count:27 |
| Dielectric Constant | 3.10 - 5.60 | 3.10 - 5.60 | Average value: 4.05 Grade Count:28 |
| 4.10 - 5.00 @Temperature 100 - 250 °C | 4.10 - 5.00 @Temperature 212 - 482 °F | Average value: 4.55 Grade Count:5 | |
| 4.10 - 5.00 @Frequency 1000 - 1.00e+9 Hz | 4.10 - 5.00 @Frequency 1000 - 1.00e+9 Hz | Average value: 4.55 Grade Count:5 | |
| Dielectric Strength | 1.54 - 56.0 kV/mm | 39.0 - 1420 kV/in | Average value: 32.4 kV/mm Grade Count:24 |
| 26.0 - 41.0 kV/mm @Temperature 120 - 200 °C | 660 - 1040 kV/in @Temperature 248 - 392 °F | Average value: 32.1 kV/mm Grade Count:3 | |
| 26.0 - 41.0 kV/mm @Thickness 0.800 - 3.20 mm | 660 - 1040 kV/in @Thickness 0.0315 - 0.126 in | Average value: 32.1 kV/mm Grade Count:3 | |
| Dissipation Factor | 0.00100 - 0.340 | 0.00100 - 0.340 | Average value: 0.0194 Grade Count:27 |
| 0.00500 - 0.0450 @Temperature 100 - 250 °C | 0.00500 - 0.0450 @Temperature 212 - 482 °F | Average value: 0.0171 Grade Count:5 | |
| 0.00500 - 0.0450 @Frequency 1000 - 1.00e+9 Hz | 0.00500 - 0.0450 @Frequency 1000 - 1.00e+9 Hz | Average value: 0.0171 Grade Count:5 | |
| Arc Resistance | 124 - 182 sec | 124 - 182 sec | Average value: 147 sec Grade Count:7 |
| Comparative Tracking Index | 100 - 249 V | 100 - 249 V | Average value: 177 V Grade Count:24 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 0.000 - 16.2 μm/m-°C | 0.000 - 9.00 μin/in-°F | Average value: 4.08 μm/m-°C Grade Count:28 |
| -5.00 - 6.00 μm/m-°C @Temperature 55.0 - 260 °C | -2.78 - 3.33 μin/in-°F @Temperature 131 - 500 °F | Average value: 1.04 μm/m-°C Grade Count:7 | |
| -5.00 - 6.00 μm/m-°C @Thickness 2.00 - 4.00 mm | -2.78 - 3.33 μin/in-°F @Thickness 0.0787 - 0.157 in | Average value: 1.04 μm/m-°C Grade Count:7 | |
| CTE, linear, Transverse to Flow | 11.0 - 88.0 μm/m-°C | 6.11 - 48.9 μin/in-°F | Average value: 57.5 μm/m-°C Grade Count:27 |
| 71.0 - 110 μm/m-°C @Temperature 55.0 - 260 °C | 39.4 - 61.1 μin/in-°F @Temperature 131 - 500 °F | Average value: 90.4 μm/m-°C Grade Count:7 | |
| 71.0 - 110 μm/m-°C @Thickness 2.00 - 4.00 mm | 39.4 - 61.1 μin/in-°F @Thickness 0.0787 - 0.157 in | Average value: 90.4 μm/m-°C Grade Count:7 | |
| Melting Point | 280 - 370 °C | 536 - 698 °F | Average value: 331 °C Grade Count:32 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 - 300 °C | 410 - 572 °F | Average value: 266 °C Grade Count:9 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 - 310 °C | 400 - 590 °F | Average value: 268 °C Grade Count:44 |
| Deflection Temperature at 8.0 MPa | 159 - 244 °C | 318 - 471 °F | Average value: 207 °C Grade Count:8 |
| Vicat Softening Point | 160 - 252 °C | 320 - 486 °F | Average value: 201 °C Grade Count:8 |
| Glass Transition Temp, Tg | 120 °C | 248 °F | Average value: 120 °C Grade Count:5 |
| UL RTI, Electrical | 130 - 240 °C | 266 - 464 °F | Average value: 224 °C Grade Count:11 |
| UL RTI, Mechanical with Impact | 130 - 220 °C | 266 - 428 °F | Average value: 204 °C Grade Count:11 |
| UL RTI, Mechanical without Impact | 130 - 240 °C | 266 - 464 °F | Average value: 233 °C Grade Count:8 |
| Flammability, UL94 | V-0 | V-0 | Grade Count:38 |
| Oxygen Index | 38.0 - 51.0 % | 38.0 - 51.0 % | Average value: 44.5 % Grade Count:16 |
| Glow Wire Test | 800 - 960 °C | 1470 - 1760 °F | Average value: 923 °C Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 20.0 - 150 °C | 68.0 - 302 °F | Average value: 70.2 °C Grade Count:14 |
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Average value: 62.0 °C Grade Count:10 |
| Nozzle Temperature | 290 - 365 °C | 554 - 689 °F | Average value: 328 °C Grade Count:4 |
| Die Temperature | 290 - 370 °C | 554 - 698 °F | Average value: 337 °C Grade Count:11 |
| Melt Temperature | 270 - 399 °C | 518 - 750 °F | Average value: 336 °C Grade Count:37 |
| Mold Temperature | 30.0 - 160 °C | 86.0 - 320 °F | Average value: 87.7 °C Grade Count:27 |
| Injection Velocity | 150 mm/sec | 5.91 in/sec | Average value: 150 mm/sec Grade Count:4 |
| Drying Temperature | 149 - 170 °C | 300 - 338 °F | Average value: 150 °C Grade Count:28 |
| Dry Time | 3.00 - 8.00 hour | 3.00 - 8.00 hour | Average value: 4.64 hour Grade Count:28 |
| Moisture Content | 0.0100 % | 0.0100 % | Average value: 0.0100 % Grade Count:21 |
| Dew Point | -40.0 - -28.9 °C | -40.0 - -20.0 °F | Average value: -35.1 °C Grade Count:9 |
| Injection Pressure | 34.5 - 150 MPa | 5000 - 21800 psi | Average value: 95.7 MPa Grade Count:16 |
| Hold Pressure | 48.0 - 150 MPa | 6960 - 21800 psi | Average value: 91.9 MPa Grade Count:11 |
| Back Pressure | 3.00 - 3.00 MPa | 435 - 435 psi | Average value: 3.00 MPa Grade Count:9 |
| Screw Speed | 80.0 - 200 rpm | 80.0 - 200 rpm | Average value: 140 rpm Grade Count:7 |
| Hot-Working Temperature | 285 - 370 °C | 545 - 698 °F | Average value: 323 °C Grade Count:5 |