- 密度 [g/cm3]: 0.92
- 缺口沖擊強度: 47.5
- 彎曲強度 [MPa]: 120.0
- 彎曲模量 [MPa]: 3.50
- 熱變形溫度 [℃]: 160.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D792 | ||
| 0.920 g/cc | 0.0332 lb/in3 | ISO 1183 | |||
| Water Absorption | <= 0.10 % | <= 0.10 % | DIN 53495 | ||
| <= 0.10 % | <= 0.10 % | 20°C; ASTM D570-81 | |||
| <= 0.10 % | <= 0.10 % | 100°C; ASTM D570-81 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 35.0 MPa | 5080 psi | EN ISO 2039-1 | ||
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | MD; DIN EN ISO 527 | ||
| 120 MPa | 17400 psi | CD; DIN EN ISO 527 | |||
| 180 MPa | 26100 psi | ASTM D638M-92 | |||
| Elongation at Break | 16.6 % | 16.6 % | ASTM D638M-92 | ||
| 20 % | 20 % | MD; DIN EN ISO 527 | |||
| 20 % | 20 % | CD; DIN EN ISO 527 | |||
| Tensile Modulus | 4.20 GPa | 609 ksi | MD; DIN EN ISO 527 | ||
| 4.20 GPa | 609 ksi | CD; DIN EN ISO 527 | |||
| 5.00 GPa | 725 ksi | ASTM D638M-93 | |||
| Flexural Strength | 80.0 MPa | 11600 psi | MD; DIN EN ISO 178 | ||
| 80.0 MPa | 11600 psi | CD; DIN EN ISO 178 | |||
| 107.7 MPa | 15620 psi | ASTM D790M-93 | |||
| Flexural Modulus | 3.50 GPa | 508 ksi | MD; DIN EN ISO 178 | ||
| 3.50 GPa | 508 ksi | CD; DIN EN ISO 178 | |||
| 3.60 GPa | 522 ksi | ASTM D790M-93 | |||
| Compressive Strength | >= 300 MPa | >= 43500 psi | Normal to Plane; EN ISO 604 | ||
| Izod Impact, Notched | 47.5 J/cm | 89.0 ft-lb/in | ASTM D256-93a | ||
| 75.0 J/cm @Temperature -40.0 °C | 141 ft-lb/in @Temperature -40.0 °F | ASTM D256-93a | |||
| Izod Impact, Notched (ISO) | 400 kJ/m2 | 190 ft-lb/in2 | 22 J; EN ISO 180/2 ep b | ||
| 600 kJ/m2 @Temperature -40.0 °C | 286 ft-lb/in2 @Temperature -40.0 °F | 22 J; EN ISO 180/2 ep b | |||
| Izod Impact, Unnotched (ISO) | NB | NB | 22 J; EN ISO 180/2 ep | ||
| Charpy Impact Unnotched | NB | NB | EN ISO 179/2 ep | ||
| NB | NB | Low Temp; EN ISO 179/2 ep | |||
| Charpy Impact, Notched | 12.0 J/cm2 | 57.1 ft-lb/in2 | EN ISO 179/2 ep b | ||
| Tensile Impact Strength | 1000 kJ/m2 | 476 ft-lb/in2 | MD; EN ISO 8256 | ||
| 1000 kJ/m2 | 476 ft-lb/in2 | CD; EN ISO 8256 | |||
| Puncture Energy | 14.1 J | 10.4 ft-lb | -40°C High Speed Puncture Energy; ASTM D3763-97a | ||
| 17.6 J | 13.0 ft-lb | 70°C High Speed Puncture Energy; ASTM D3763-97a | |||
| 21.6 J | 15.9 ft-lb | 100°C High Speed Puncture Energy; ASTM D3763-97a | |||
| 40.0 J | 29.5 ft-lb | Puncture Impact; 52 J; 2.1 mm; ISO 6603 | |||
| Torsional Stiffness | 1200 MPa | 174000 psi | DIN EN ISO 6721 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 41.0 μm/m-°C @Temperature 20.0 °C | 22.8 μin/in-°F @Temperature 68.0 °F | Temp range not reported; ASTM D696 | ||
| 68.0 μm/m-°C @Temperature 20.0 - 80.0 °C | 37.8 μin/in-°F @Temperature 68.0 - 176 °F | DIN 53752 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | flatwise; EN ISO 75-2B | ||
| 160 °C | 320 °F | ASTM D648-82/88 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 102 °C | 216 °F | ASTM D648-82/88 | ||
| 102 °C | 216 °F | flatwise; EN ISO 75-2A | |||
| Vicat Softening Point | 175 °C | 347 °F | 50K/h; DIN EN ISO 306 | ||
| Descriptive Properties | |||||
| Fire Behavior of Building Materials | Passed B 2 | DIN 4102 | |||