- 熔體流動速率 [g/10min]: 0.5
- 拉伸強度 [MPa]: 27.0
- 彎曲模量 [MPa]: 1.242
- 熱變形溫度 [℃]: 88.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | 2.16 kg at 230C; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 27.0 MPa | 3920 psi | at 23C; ASTM D638 | ||
| Flexural Modulus | 1.242 GPa | 180.1 ksi | at 23C; ADST D790A | ||
| Izod Impact, Notched | NB | NB | 1/8” (3 mm) notched bar; ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 88.0 °C | 190 °F | ASTM D648 | ||
| Descriptive Properties | |||||
| process | Blow Molding | ||||
| Pipe Extrusion | |||||
| Sheet Extrusion | |||||
| region | Mexico | ||||
| US & Canada | |||||