- 熔體流動(dòng)速率 [g/10min]: 4.5
- 密度 [g/cm3]: 1.14
- 彎曲模量 [MPa]: 6.50
- 熱變形溫度 [℃]: 148.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0095 cm/cm | 0.0095 in/in | Borealis Method | ||
| Melt Flow | 4.5 g/10 min @Load 2.16 kg, Temperature 230 °C | 4.5 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 106 MPa | 15400 psi | ISO 527-2 | ||
| Elongation at Break | 3.2 % | 3.2 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 7.50 GPa | 1090 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Strength | 145 MPa | 21000 psi | ISO 178 | ||
| Flexural Modulus | 6.50 GPa | 943 ksi | 2mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 5.40 J/cm2 @Temperature -20.0 °C | 25.7 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | ||
| 5.90 J/cm2 @Temperature 23.0 °C | 28.1 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | ||
| 1.10 J/cm2 @Temperature 23.0 °C | 5.23 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 148 °C | 298 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 158 °C | 316 °F | ISO 75-2 | ||
| Vicat Softening Point | 139 °C @Load 5.10 kg | 282 °F @Load 11.2 lb | ISO 306 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 230 - 280 °C | 446 - 536 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 1667 - 3333 mm/sec | 65.63 - 131.2 in/sec | |||
| Hold Pressure | 3.00 - 6.00 MPa | 435 - 870 psi | |||
| Descriptive Properties | |||||
| Back Pressure | as low as possible | ||||
| Emission (μgC/g) | < 50 | VDA 277 | |||
| Fogging (mg) | < 2 | DIN 75201 | |||
| Screw Speed | low to medium | ||||