- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 29.0
- 硬度: 82.0
- 熱變形溫度 [℃]: 80.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 230 °C | 20 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 82 | 82 | ISO 2039-2 | ||
| Tensile Strength, Yield | 29.0 MPa | 4210 psi | 50mm/min; ISO 527-2 | ||
| Elongation at Yield | 11 % | 11 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 1.15 GPa | 167 ksi | 1mm/min; ISO 527-2 | ||
| Charpy Impact, Notched | 0.600 J/cm2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | ISO 75-2 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | <= 5.0 % | <= 5.0 % | Borealis Method | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | <= 130 °C | <= 266 °F | reheat temperature | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 30.0 - 40.0 °C | 86.0 - 104 °F | |||
| Injection Pressure | 0.500 - 2.00 MPa | 72.5 - 290 psi | |||
| Hold Pressure | 20.0 - 50.0 MPa | 2900 - 7250 psi | |||
| Descriptive Properties | |||||
| Injection Velocity | high | ||||