- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 25.0
- 彎曲模量 [MPa]: 0.800
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 |
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 13.5 % | 13.5 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 0.900 GPa | 131 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 0.800 GPa | 116 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm2 @Temperature -20.0 °C | 19.0 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |
| NB @Temperature 0.000 °C | NB @Temperature 32.0 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.200 J/cm2 @Temperature -20.0 °C | 0.952 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA |
| 0.350 J/cm2 @Temperature 0.000 °C | 1.67 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eA | |
| 2.00 J/cm2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 150 μm/m-°C | 83.3 μin/in-°F | (0°C/70°C); DIN 53752 |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft2-°F | DIN 52612 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 180 - 210 °C | 356 - 410 °F | cylinder |
| Die Temperature | 210 - 220 °C | 410 - 428 °F | |
| Melt Temperature | 220 °C | 428 °F | |
| Head Temperature | 210 - 220 °C | 410 - 428 °F | |