- 熔體流動(dòng)速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.9
- 彎曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in3 | base resin; ISO 1183 |
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Antiblock Level | 1800 ppm | 1800 ppm | SiO2; Borealis Method |
| Slip Level | 2000 ppm | 2000 ppm | EAA; Borealis Method |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 - 750 % | 550 - 750 % | ISO 527-3 |
| Film Elongation at Break, TD | 550 - 750 % | 550 - 750 % | ISO 527-3 |
| Tensile Modulus | 0.500 - 0.600 GPa | 72.5 - 87.0 ksi | MD/TD; ISO 527-3 |
| Flexural Modulus | 1.00 GPa | 145 ksi | ISO 178 |
| Dart Drop, Total Energy | 17.0 J @Thickness 0.0500 mm | 12.5 ft-lb @Thickness 0.00197 in | 1100N; ISO 7765-2 |
| Coefficient of Friction | 0.20 - 0.30 | 0.20 - 0.30 | film/film; ISO 8295 |
| Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 148 - 154 °C | 298 - 309 °F | DSC; ISO 3146 |
| Vicat Softening Point | 139 °C @Load 1.02 kg | 282 °F @Load 2.25 lb | A50; ISO 306 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 2.0 % | <= 2.0 % | ASTM D1003 |
| Gloss | >= 120 % | >= 120 % | 20° of arc; ASTM D2457 |