- 彎曲模量 [MPa]: 7.30
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Filler Content | 30 % | 30 % | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-2 | ||
| Elongation at Break | 2.4 % | 2.4 % | ISO 527-2 | ||
| Tensile Modulus | 8.10 GPa | 1170 ksi | ISO 527-2 | ||
| Flexural Strength | 170 MPa | 24700 psi | 3.3% strain; ISO 178 | ||
| Flexural Modulus | 7.30 GPa | 1060 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 4.20 J/cm2 @Temperature 23.0 °C | 20.0 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1fU | ||
| 4.70 J/cm2 @Temperature -30.0 °C | 22.4 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1fU | |||
| 5.50 J/cm2 @Temperature 23.0 °C | 26.2 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.65 J/cm2 @Temperature 23.0 °C | 7.85 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Dart Drop, Total Energy | 12.0 J @Temperature 23.0 °C | 8.85 ft-lb @Temperature 73.4 °F | 3200N, 6mm deflection; ISO 6603 | ||
| Processing Properties | Metric | English | Comments | ||
| Feed Temperature | 220 - 240 °C | 428 - 464 °F | |||
| Melt Temperature | 240 - 270 °C | 464 - 518 °F | |||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |||
| Injection Velocity | 20.0 - 30.0 mm/sec | 0.787 - 1.18 in/sec | |||
| Injection Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Screw Speed | 30 - 150 rpm | 30 - 150 rpm | |||
| Descriptive Properties | |||||
| Back Pressure | 0-10% of injection pressure | ||||
| Hold Pressure | 50-70% of injection pressure | ||||