- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.9
- 彎曲模量 [MPa]: 1.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.900 - 0.910 g/cc | 0.0325 - 0.0329 lb/in3 | ISO 1183 | ||
| Melt Flow | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Antiblock Level | 1800 ppm | 1800 ppm | SiO2; Borealis Method | ||
| Slip Level | 1800 ppm | 1800 ppm | EAA; Borealis Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 550 - 750 % | 550 - 750 % | ISO 527-3 | ||
| Film Elongation at Break, TD | 550 - 750 % | 550 - 750 % | ISO 527-3 | ||
| Tensile Modulus | 0.500 - 0.600 GPa | 72.5 - 87.0 ksi | MD/TD; ISO 527-3 | ||
| Flexural Modulus | 1.00 GPa | 145 ksi | ISO 178 | ||
| Dart Drop, Total Energy | 17.0 J @Thickness 0.0500 mm | 12.5 ft-lb @Thickness 0.00197 in | 1100N; ISO 7765-2 | ||
| Coefficient of Friction | 0.10 - 0.20 | 0.10 - 0.20 | film/film; ISO 8295 | ||
| Film Tensile Strength at Break, MD | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527-3 | ||
| Film Tensile Strength at Break, TD | 25.0 - 45.0 MPa | 3630 - 6530 psi | ISO 527-3 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 148 - 154 °C | 298 - 309 °F | DSC; ISO 3146 | ||
| Vicat Softening Point | 139 °C @Load 1.02 kg | 282 °F @Load 2.25 lb | A50; ISO 306 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | <= 2.0 % | <= 2.0 % | ASTM D1003 | ||
| Gloss | >= 120 % | >= 120 % | 20° of arc; ASTM D2457 | ||
| Descriptive Properties | |||||
| Antistatic Level (ppm) | < 2000 | Borealis Method | |||