- 熔體流動速率 [g/10min]: 24.0
- 密度 [g/cm3]: 1.14
- 拉伸強度 [MPa]: 31.0
- 彎曲模量 [MPa]: 3.25
- 熱變形溫度 [℃]: 125.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | Borealis Method; average process | ||
| Melt Flow | 24 g/10 min @Load 2.16 kg, Temperature 230 °C | 24 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 102 g/10 min @Load 5.00 kg, Temperature 230 °C | 102 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 91.0 MPa | 13200 psi | 358 N/30s; ISO 2039 | ||
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 3.0 % | 3.0 % | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 3.30 GPa | 479 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Modulus | 3.25 GPa | 471 ksi | 2mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 1.30 J/cm2 @Temperature -20.0 °C | 6.19 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | ||
| 2.20 J/cm2 @Temperature 23.0 °C | 10.5 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.120 J/cm2 @Temperature -20.0 °C | 0.571 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | ||
| 0.150 J/cm2 @Temperature 23.0 °C | 0.714 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-2 | ||
| Vicat Softening Point | 95.0 °C @Load 5.10 kg | 203 °F @Load 11.2 lb | ISO 306 | ||
| 155 °C @Load 1.02 kg | 311 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Emission (μgC/g) | 33 | VDA 277 | |||
| Fogging (mg) | 0.9 | 100°C, 16h; DIN 75201 | |||
| Screw Speed | low to medium | ||||