- 熔體流動(dòng)速率 [g/10min]: 16.0
- 密度 [g/cm3]: 1.27
- 拉伸強(qiáng)度 [MPa]: 23.0
- 彎曲模量 [MPa]: 2.60
- 熱變形溫度 [℃]: 113.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | average process; in flow; 150x80x2mm | ||
| 0.010 cm/cm | 0.010 in/in | average process; cross flow; 150x80x2mm | |||
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 230 °C | 16 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | 50mm/min; ISO 527-2 | ||
| Tensile Modulus | 2.80 GPa | 406 ksi | 1mm/min; ISO 527-2 | ||
| Flexural Modulus | 2.60 GPa | 377 ksi | 2mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 3.50 J/cm2 | 16.7 ft-lb/in2 | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.210 J/cm2 @Temperature 23.0 °C | 0.999 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 113 °C | 235 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | ISO 75-2 | ||
| Vicat Softening Point | 105 °C @Load 5.10 kg | 221 °F @Load 11.2 lb | ISO 306 | ||
| 155 °C @Load 1.02 kg | 311 °F @Load 2.25 lb | ISO 306 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 220 - 260 °C | 428 - 500 °F | mass temperature | ||
| Feed Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Injection Velocity | 100 - 200 mm/sec | 3.94 - 7.87 in/sec | |||
| Hold Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi | |||
| Descriptive Properties | |||||
| Back Pressure | low to medium | ||||
| Screw Speed | low to medium | ||||