- 熔體流動速率 [g/10min]: 1.9
- 密度 [g/cm3]: 0.902
- 拉伸強度 [MPa]: 26.0
- 熱變形溫度 [℃]: 86.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in3 | ISO 1183 |
| Melt Flow | 1.9 g/10 min @Load 2.16 kg, Temperature 230 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50mm/min; ISO 527-2 |
| Elongation at Yield | 13 % | 13 % | 50mm/min; ISO 527-2 |
| Tensile Modulus | 1.15 GPa | 167 ksi | 1mm/min; ISO 527-2 |
| Charpy Impact, Notched | 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | ISO 75-2 |
| Processing Properties | Metric | English | Comments |
| Middle Barrel Temperature | 190 - 220 °C | 374 - 428 °F | |
| Die Temperature | 180 - 220 °C | 356 - 428 °F | |
| Melt Temperature | 180 - 220 °C | 356 - 428 °F | |