- 熔體流動速率 [g/10min]: 0.3
- 密度 [g/cm3]: 0.928
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.928 g/cc | 0.0335 lb/in3 | ISO 1183 | ||
| Environmental Stress Crack Resistance | >= 250 hour @Temperature 50.0 °C | >= 250 hour @Temperature 122 °F | Igepal 100%; F20; ASTM D1693-B | ||
| Thermal Stress Crack Resistance | >= 1.00 hour @Temperature 105 °C | >= 1.00 hour @Temperature 221 °F | IEC 60811-4-2/A | ||
| Oxidative Induction Time (OIT) | 50 min @Temperature 200 °C | 50 min @Temperature 392 °F | IEC 60811-4-2/B | ||
| Melt Flow | 0.30 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.30 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 53 | 53 | 1s; ISO 868 | ||
| Tensile Strength at Break | 17.0 MPa | 2470 psi | ISO 527 | ||
| Elongation at Break | 600 % | 600 % | ISO 527 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 2.3 @Frequency 1.00e+6 Hz | 2.3 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dielectric Strength | 22.0 kV/mm @Frequency 1000 Hz | 559 kV/in @Frequency 1000 Hz | IEC 60250 | ||
| Dissipation Factor | 0.00015 @Frequency 1.00e+6 Hz | 0.00015 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D746 | ||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 70.0 - 100 °C | 158 - 212 °F | conductor preheating temperature; 2400 m/min line speed | ||
| Middle Barrel Temperature | 165 - 230 °C | 329 - 446 °F | |||
| Melt Temperature | 220 - 240 °C | 428 - 464 °F | |||
| Head Temperature | 230 °C | 446 °F | |||
| Descriptive Properties | |||||
| Petroleum Jelly Absorption (%) | 8 | IEC 60811-4-2 | |||