- 熔體流動速率 [g/10min]: 25.0
- 密度 [g/cm3]: 0.905
- 拉伸強度 [MPa]: 23.0
- 硬度: 67.0
- 熱變形溫度 [℃]: 72.0
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.905 g/cc | 0.0327 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | |||
| Melt Flow | 25 g/10 min @Load 2.16 kg, Temperature 230 °C | 25 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 67 | 67 | ISO 2039-2 | ||
| Tensile Strength, Yield | 23.0 MPa | 3340 psi | ISO 527-2 | ||
| Elongation at Yield | 14 % | 14 % | ISO 527-2 | ||
| Tensile Modulus | 0.900 GPa | 131 ksi | ISO 527-2 | ||
| Charpy Impact, Notched | 0.200 J/cm2 @Temperature -10.0 °C | 0.952 ft-lb/in2 @Temperature 14.0 °F | ISO 179/1eA | ||
| 0.400 J/cm2 @Temperature 0.000 °C | 1.90 ft-lb/in2 @Temperature 32.0 °F | ISO 179/1eA | |||
| 0.800 J/cm2 @Temperature 23.0 °C | 3.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Dart Drop, Total Energy | 5.00 J @Temperature -10.0 °C | 3.69 ft-lb @Temperature 14.0 °F | ISO 6603-2 | ||
| 20.0 J @Temperature 0.000 °C | 14.8 ft-lb @Temperature 32.0 °F | ISO 6603-2 | |||
| 35.0 J @Temperature 23.0 °C | 25.8 ft-lb @Temperature 73.4 °F | ISO 6603-2 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 72.0 °C | 162 °F | ISO 75-2 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 21 % | 21 % | 1mm plaque; Borealis Method | ||
| Transmission, Visible | 90.0 % | 90.0 % | transparent; thickness not quantified | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |||
| Mold Temperature | 20.0 - 40.0 °C | 68.0 - 104 °F | |||
| Hold Pressure | 20.0 - 50.0 MPa | 2900 - 7250 psi | |||
| Descriptive Properties | |||||
| Injection Velocity | high | ||||