- 熔體流動速率 [g/10min]: 13.0
- 密度 [g/cm3]: 0.97
- 拉伸強度 [MPa]: 26.3
- 彎曲模量 [MPa]: 2.10
- 熱變形溫度 [℃]: 114.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.970 g/cc | 0.0350 lb/in3 | ISO 1183 | ||
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C | 13 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 | ||
| 74.2 g/10 min @Load 5.00 kg, Temperature 230 °C | 74.2 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 66.0 MPa | 9570 psi | H 385/30; ISO 2039 | ||
| Tensile Strength, Yield | 26.3 MPa | 3810 psi | At 50 mm/min; ISO 527-2 | ||
| Elongation at Yield | 3.3 % | 3.3 % | At 50 mm/min; ISO 527-2 | ||
| Tensile Modulus | 2.00 GPa | 290 ksi | At 1 mm/min; ISO 527-2 | ||
| Flexural Modulus | 2.10 GPa | 305 ksi | At 2 mm/min; ISO 178 | ||
| Charpy Impact Unnotched | 12.0 J/cm2 | 57.1 ft-lb/in2 | ISO 179/1eU | ||
| 6.00 J/cm2 @Temperature -20.0 °C | 28.6 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.690 J/cm2 | 3.28 ft-lb/in2 | ISO 179/1eA | ||
| 0.300 J/cm2 @Temperature -20.0 °C | 1.43 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 114 °C | 237 °F | ISO 75-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 59.0 °C | 138 °F | ISO 75-2 | ||
| Vicat Softening Point | 73.0 °C | 163 °F | B (50N); ISO 306 | ||
| 151 °C | 304 °F | A (10N); ISO 306 | |||
| Shrinkage | 1.3 % | 1.3 % | Borealis Method | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |||
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |||
| Descriptive Properties | |||||
| Emissions, ug C/g | 48 | VDA 277 | |||
| Fogging, mg | 0.2 | At 100°C/ 16 hours | |||