- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.14
- 拉伸強度 [MPa]: 103.0
- 彎曲模量 [MPa]: 5.90
- 熱變形溫度 [℃]: 162.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | ISO 1183 |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| 25 g/10 min @Load 5.00 kg, Temperature 230 °C | 25 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 132 MPa | 19100 psi | H 385/30; ISO 2039 |
| Tensile Strength, Yield | 103 MPa | 14900 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 2.8 % | 2.8 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 7.14 GPa | 1040 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 5.90 GPa | 856 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | 4.00 J/cm2 | 19.0 ft-lb/in2 | ISO 179/1eU |
| 3.70 J/cm2 @Temperature -20.0 °C | 17.6 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.740 J/cm2 | 3.52 ft-lb/in2 | ISO 179/1eA |
| 0.610 J/cm2 @Temperature -20.0 °C | 2.90 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 162 °C | 324 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | ISO 75-2 |
| Vicat Softening Point | 136 °C | 277 °F | B (50N); ISO 306 |
| 165 °C | 329 °F | A (10N); ISO 306 | |
| Shrinkage | 0.80 % | 0.80 % | Borealis Method |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 260 °C | 410 - 500 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |