- 熔體流動速率 [g/10min]: 13.0
- 密度 [g/cm3]: 1.07
- 拉伸強度 [MPa]: 22.99
- 彎曲模量 [MPa]: 2.10
- 熱變形溫度 [℃]: 97.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.07 g/cc | 0.0387 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | Borealis Method |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 230 °C | 13 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.99 MPa | 3335 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 5.1 % | 5.1 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 2.00 GPa | 290 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 2.10 GPa | 305 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| 7.60 J/cm2 @Temperature -20.0 °C | 36.2 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 3.40 J/cm2 | 16.2 ft-lb/in2 | ISO 179/1eA |
| 0.250 J/cm2 @Temperature -30.0 °C | 1.19 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| 0.300 J/cm2 @Temperature -20.0 °C | 1.43 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 97.0 °C | 207 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 53.0 °C | 127 °F | ISO 75-2 |
| Vicat Softening Point | 52.0 °C | 126 °F | B (50N); ISO 306 |
| 130 °C | 266 °F | A (10N); ISO 306 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |