- 熔體流動速率 [g/10min]: 12.0
- 密度 [g/cm3]: 0.96
- 缺口沖擊強度: 25.0
- 拉伸強度 [MPa]: 20.99
- 彎曲模量 [MPa]: 1.70
- 熱變形溫度 [℃]: 100.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.960 g/cc | 0.0347 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0011 cm/cm | 0.0011 in/in | Borealis Method |
| Melt Flow | 12 g/10 min @Load 2.16 kg, Temperature 230 °C | 12 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| 45 g/10 min @Load 5.00 kg, Temperature 230 °C | 45 g/10 min @Load 11.0 lb, Temperature 446 °F | ISO 1133 | |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 42.0 MPa | 6090 psi | H385/30; ISO 2039 |
| Tensile Strength, Yield | 20.99 MPa | 3045 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 6.0 % | 6.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.85 GPa | 268 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 1.70 GPa | 247 ksi | At 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 25.0 kJ/m2 | 11.9 ft-lb/in2 | ISO 180/1A |
| 5.00 kJ/m2 @Temperature 0.000 °C | 2.38 ft-lb/in2 @Temperature 32.0 °F | ISO 180/1A | |
| Charpy Impact Unnotched | 16.0 J/cm2 | 76.1 ft-lb/in2 | ISO 179/1eU |
| 6.00 J/cm2 @Temperature -20.0 °C | 28.6 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 2.00 J/cm2 | 9.52 ft-lb/in2 | ISO 179/1eA |
| 0.450 J/cm2 @Temperature -20.0 °C | 2.14 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 100 °C | 212 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-2 |
| Vicat Softening Point | 54.0 °C | 129 °F | B (50N); ISO 306 |
| 136 °C | 277 °F | A (10N); ISO 306 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |