- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 0.99
- 拉伸強度 [MPa]: 17.0
- 彎曲模量 [MPa]: 1.10
- 熱變形溫度 [℃]: 87.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.990 g/cc | 0.0358 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0095 - 0.0085 cm/cm | 0.0095 - 0.0085 in/in | Borealis Method |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 230 °C | 10 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 35.0 MPa | 5080 psi | At 132 N/10 sec; ISO 2039 |
| Tensile Strength, Yield | 17.00 MPa | 2465 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Break | 450 % | 450 % | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 7.0 % | 7.0 % | At 50 mm/min; ISO 527-2 |
| Tensile Modulus | 1.15 GPa | 167 ksi | At 1 mm/min; ISO 527-2 |
| Flexural Modulus | 1.10 GPa | 160 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB @Temperature -20.0 °C | NB @Temperature -4.00 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 6.50 J/cm2 | 30.9 ft-lb/in2 | ISO 179/1eA |
| 0.500 J/cm2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |
| 0.650 J/cm2 @Temperature -20.0 °C | 3.09 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | <= 85.0 μm/m-°C @Temperature -30.0 - 80.0 °C | <= 47.2 μin/in-°F @Temperature -22.0 - 176 °F | Borealis Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 °C | 120 °F | ISO 75-2 |
| Vicat Softening Point | 126 °C | 259 °F | A (10N); ISO 306 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 - 260 °C | 428 - 500 °F | Polymer Mass Temp |
| Mold Temperature | 30.0 - 50.0 °C | 86.0 - 122 °F | |
- 關(guān)鍵詞:
- 供應(yīng)
- PP
- Borealis Daplen? EE115T TPO Compound