- 熔體流動速率 [g/10min]: 22.0
- 拉伸強度 [MPa]: 14.0
- 彎曲模量 [MPa]: 0.400
- 熱變形溫度 [℃]: 35.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 230 °C | 22 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133/DIN 5335 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ISO 527-2 |
| Elongation at Yield | 15 % | 15 % | ISO 527-2 |
| Tensile Modulus | 0.450 GPa | 65.3 ksi | ISO 527-2 |
| Flexural Modulus | 0.400 GPa | 58.0 ksi | DIN 53457/ISO 178 |
| Charpy Impact, Notched | 2.50 J/cm2 | 11.9 ft-lb/in2 | ISO 179/1eA |
| 0.200 J/cm2 @Temperature -20.0 °C | 0.952 ft-lb/in2 @Temperature -4.00 °F | ISO 179/1eA | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 35.0 °C | 95.0 °F | ISO 75 A |
| Deflection Temperature at 1.8 MPa (264 psi) | 52.0 °C | 126 °F | ISO 75 B |