- 密度 [g/cm3]: 1.5
- 缺口沖擊強度: 0.64
- 彎曲強度 [MPa]: 68.0
- 彎曲模量 [MPa]: 7.40
- 硬度: 106.0
- 熱變形溫度 [℃]: 152.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in3 | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 68.0 MPa | 9860 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 96.0 MPa | 13900 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.83 J/cm | 5.30 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 138 °C | 280 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 229 - 246 °C | 444 - 475 °F | Approximate middle barrel temperature range |