- 密度 [g/cm3]: 1.16
- 缺口沖擊強度: 0.91
- 彎曲強度 [MPa]: 73.0
- 彎曲模量 [MPa]: 6.00
- 硬度: 103.0
- 熱變形溫度 [℃]: 164.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0419 lb/in3 | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Ultimate | 73.0 MPa | 10600 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 115 MPa | 16700 psi | ASTM D790 |
| Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D790 |
| Izod Impact, Notched | 0.910 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 229 - 246 °C | 444 - 475 °F | Approximate middle barrel temperature range |