- 密度 [g/cm3]: 1.22
- 缺口沖擊強(qiáng)度: 0.59
- 彎曲強(qiáng)度 [MPa]: 67.0
- 彎曲模量 [MPa]: 5.80
- 硬度: 106.0
- 熱變形溫度 [℃]: 163.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 67.0 MPa | 9720 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 101 MPa | 14600 psi | ASTM D790 |
| Flexural Modulus | 5.80 GPa | 841 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.79 J/cm | 7.10 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 °C | 325 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 147 °C | 297 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 225 °C | 437 °F | Approximate middle barrel temperature. |