- 密度 [g/cm3]: 1.11
- 缺口沖擊強度: 0.69
- 彎曲強度 [MPa]: 57.0
- 彎曲模量 [MPa]: 4.00
- 硬度: 103.0
- 熱變形溫度 [℃]: 154.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in3 | |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Ultimate | 57.0 MPa | 8270 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Strength | 93.0 MPa | 13500 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.38 J/cm | 8.21 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 133 °C | 271 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 225 °C | 437 °F | Approximate middle barrel temperature. |