- 密度 [g/cm3]: 1.19
- 缺口沖擊強(qiáng)度: 0.59
- 彎曲強(qiáng)度 [MPa]: 61.0
- 彎曲模量 [MPa]: 5.60
- 硬度: 105.0
- 熱變形溫度 [℃]: 169.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 105 | 105 | ASTM D785 |
| Tensile Strength, Ultimate | 61.0 MPa | 8850 psi | ASTM D638 |
| Elongation at Break | 3.8 % | 3.8 % | ASTM D638 |
| Flexural Strength | 109 MPa | 15800 psi | ASTM D790 |
| Flexural Modulus | 5.60 GPa | 812 ksi | ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.52 J/cm | 6.59 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 169 °C | 336 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 289 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 225 °C | 437 °F | Approximate middle barrel temperature. |