- 密度 [g/cm3]: 1.08
- 缺口沖擊強度: 0.48
- 彎曲強度 [MPa]: 26.0
- 彎曲模量 [MPa]: 1.90
- 硬度: 90.0
- 熱變形溫度 [℃]: 93.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in3 | |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 90 | 90 | ASTM D785 |
| Tensile Strength, Ultimate | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 35 % | 35 % | ASTM D638 |
| Flexural Strength | 45.0 MPa | 6530 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 276 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.08 J/cm | 3.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C | 199 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | ASTM D648 |