- 密度 [g/cm3]: 1.21
- 缺口沖擊強(qiáng)度: 0.96
- 彎曲強(qiáng)度 [MPa]: 92.0
- 彎曲模量 [MPa]: 7.40
- 硬度: 106.0
- 熱變形溫度 [℃]: 179.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.21 g/cc | 0.0437 lb/in3 | |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 | 106 | ASTM D785 |
| Tensile Strength, Ultimate | 92.0 MPa | 13300 psi | ASTM D638 |
| Elongation at Break | 2.8 % | 2.8 % | ASTM D638 |
| Flexural Strength | 152 MPa | 22000 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 6.09 J/cm | 11.4 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 179 °C | 354 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 155 °C | 311 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 229 - 246 °C | 444 - 475 °F | Approximate middle barrel temperature range |