- 熔體流動速率 [g/10min]: 9.0
- 密度 [g/cm3]: 0.902
- 拉伸強度 [MPa]: 17.5
- 熱變形溫度 [℃]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.902 g/cc | 0.0326 lb/in3 | |
| Melt Flow | 9.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 9.0 g/10 min @Load 4.76 lb, Temperature 446 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 17.5 MPa | 2540 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 6.0 % | 6.0 % | 50 mm/min |
| Tensile Modulus | 0.905 GPa | 131 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| Charpy Impact, Notched | 5.80 J/cm2 | 27.6 ft-lb/in2 | Partial Break |
| 0.640 J/cm2 @Temperature -30.0 °C | 3.05 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 163 °C | 325 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 43.0 °C | 109 °F | |
| Vicat Softening Point | 50.0 °C | 122 °F | 50°C/hr; 50N |