- 密度 [g/cm3]: 1.23
- 缺口沖擊強度: 5.0
- 拉伸強度 [MPa]: 20.0
- 彎曲模量 [MPa]: 2.10
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ISO 1183 |
| Filler Content | 40 % | 40 % | ISO 3451 / 1 |
| Melt Index of Compound | 10 g/10 min @Load 2.16 kg, Temperature 230 °C | 10 g/10 min @Load 4.76 lb, Temperature 446 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 74 | 74 | ISO 868 |
| Tensile Strength, Yield | 20.0 MPa | 2900 psi | ISO 527 |
| Elongation at Break | 20 % | 20 % | ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m2 | 6.19 ft-lb/in2 | ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75 |
| Vicat Softening Point | 78.0 °C | 172 °F | 49 N; ISO 306 |